Heat Shrinkable Breakouts - 2 Core

Code: N/A

Provide sealing protection and strain relief over multi-core cable crutch.

Technical Data
   
Property Test Method Standard Value
Insulated Breakout Oil Resistant Breakout Semi-conductive Breakout
Tensile Strength ASTM-D-638 ≥12MPa ≥12MPa ≥12MPa
Elongation at Break (120℃,168 hrs) ASTM-D-638 ≥300% ≥300% ≥300%
Tensile Strength after Aging (120℃,168 hrs) ASTM-D-638 ≥10MPa ≥10MPa ≥10MPa
Elongation at Break after Aging ASTM-D-638ASTM-D-638ASTM-D-638 ≥230% ≥230% ≥230%
Tensile Strength Variation after Dipping  ASTM-D-638ASTM-D-638 ≤20%
Elongation at Break  after Dipping ASTM-D-638 ≥230%
Dielectric Strength IEC 60243 ≥15kV/mm ≥15kV/mm
Water Absorption ISO 62 ≤0.1% ≤0.1%≤0.1% ≤0.1%
Volume Resistivity IEC 60093 ≥1×1013Ω·cm ≥1×1013Ω·cm ≥1×1013Ω·cm
Brittle Temperature ISO 974 -40℃ -40℃ -40℃
Heat Shock 160℃,4h No Crack No Crack No Crack
Hardness(Shore A) ISO 868 ≥80 ≥80 ≥80
 
2 Core
   
Cores As Supplied(mm) After Recovered
Body Diameter (D) Min Finger Diameter (d) Min Full Length (L)(±5) Body Diameter (D)Max inger Diameter (d) Min
2-cores Breakout 24 12 140 14 5
38 20 145 18 7
45 25 145 22 10
60 35 140 25 11
70 40 140 25 11
 
Features

Features

  • Coated with adhesive on the body and the fingers to form a watertight seal.
  • Flame-retardant breakouts are available.

 

Material

Cross-linked polyolefin.

Application

Used in indoor & outdoor Termination Kit.